LaMnO3

阴极材料名称

材料牌号	材料类型	信息来源
Grade	Type	Information Source
Gd0.5Sr0.5MnO3	陶瓷	Yoon.H.S,Choi.S.W, Lee.D,Kim.B.H.J Power Sources.2001(93)1
Gd0.7Ca0.3Co0.4Mn0.6O3	陶瓷	Philipps.M.B,Sammmes.N.M,Yamamoto.O.Solid State Ionics.1999(123)131.
Gd0.7Ca0.3Co0.7Mn0.3O3	陶瓷	Philipps.M.B,Sammmes.N.M,Yamamoto.O.Solid State Ionics.1999(123)131.
Gd0.7Ca0.3MnO3	陶瓷	Philipps.M.B,Sammmes.N.M,Yamamoto.O.Solid State Ionics.1999(123)131.
Gd0.7Sr0.3MnO3	陶瓷	Sakaki.Y,Takeda.Y,Kato.A.et al,Solid State Ionics.1999(118)187;Rim.H.R,Jeyng.S.K,Jung.E,et al,Mater Chem Phys.1998(52)54.
Gd0.8Sr0.2Co0.2Mn0.8O3	陶瓷	Philipps.M.B,Sammmes.N.M,Yamamoto.O.Solid State Ionics.1999(123)131.
Gd0.8Sr0.2Co0.9Mn0.1O3	陶瓷	Philipps.M.B,Sammmes.N.M,Yamamoto.O.Solid State Ionics.1999(123)131.
Gd0.8Sr0.2MnO3	陶瓷	Yoon.H.S,Choi.S.W, Lee.D,Kim.B.H.J Power Sources.2001(93)1;Philipps.M.B,Sammmes.N.M,Yamamoto.O.Solid State Ionics.1999(123)131.
La0.6Sr0.4MnO3	陶瓷	Sakaki.Y, Takeda.Y,Kato.A, Solid State Ionics.1999(118)187
La0.76Sr0.19Mn0.7Ni0.3O3	陶瓷	Wandekar.R.V,Wani.B.N,Bharadwaj.S.R. Mater Lett2005(59)2799.
La0.7Sr0.3MnO3	陶瓷	J.Mizusaki, Y.Yonemura, H.Kamata, et al,Solid State Ionics.2000(132)167;Mori M, Hiei Y,Sammes NM.The Electrochemical Society,Ync.,Pennington,p347.
La0.82Sr0.16Mn0.7Ni0.3O3	陶瓷	Kuharuangrong.S.Ceram Int.2004(30)273
La0.84Sr0.16Mn0.6Co0.4O3	陶瓷	Kuharuangrong. S,Dechakupt.T,Aungkavattana.P. Mater Lett,2004(19)497.
La0.84Sr0.16Mn0.6Fe0.4O3	陶瓷	Kuharuangrong. S,Dechakupt.T,Aungkavattana.P. Mater Lett,2004(19)497.
La0.84Sr0.16Mn0.8Co0.2O3	陶瓷	Kuharuangrong. S,Dechakupt.T,Aungkavattana.P. Mater Lett,2004(19)497.

首页上一页下一页末页第1页/ 共3页

转至页

化学成分

牌号	La	Pr	Nd	Gd	Ce	Sn	Mn	Sr	Ca	Co	Fe	Ni	O
Gd0.5Sr0.5MnO3				√			√	√					√
Gd0.7Ca0.3Co0.4Mn0.6O3				√			√		√	√			√
Gd0.7Ca0.3Co0.7Mn0.3O3				√			√		√	√			√
Gd0.7Ca0.3MnO3				√			√		√				√
Gd0.7Sr0.3MnO3				√			√	√					√
Gd0.8Sr0.2Co0.2Mn0.8O3				√			√	√		√			√
Gd0.8Sr0.2Co0.9Mn0.1O3				√			√	√		√			√
Gd0.8Sr0.2MnO3				√			√	√					√
La0.6Sr0.4MnO3	√						√	√					√
La0.76Sr0.19Mn0.7Ni0.3O3	√						√	√				√	√
La0.7Sr0.3MnO3	√						√	√					√
La0.82Sr0.16Mn0.7Ni0.3O3	√						√	√				√	√
La0.84Sr0.16Mn0.6Co0.4O3	√						√	√		√			√
La0.84Sr0.16Mn0.6Fe0.4O3	√						√	√			√		√
La0.84Sr0.16Mn0.8Co0.2O3	√						√	√		√			√

首页上一页下一页末页第1页/ 共3页

转至页

性能

材料牌号	热膨胀系数(×10-6K-1)	电导率(Scm-1)	离子电导率(Scm-1)	氧扩散系数（cm2s-1）	氧表面交换系数（cm2s-1）	ASR(Ωcm2)	信息来源
Grade	Thermal expansion coefficients	Conductivity(Scm-1)	Ionic conductivity(Scm-1)	Oxygen diffusion coefficients（cm2s-1）	Oxygen surface exchange coefficients（cm2s-1）	ASR(Ωcm2)	Information Source
Gd0.5Sr0.5MnO3	6.84	229.5(800℃)
Gd0.7Ca0.3Co0.4Mn0.6O3	10.5	37(800℃)
Gd0.7Ca0.3Co0.7Mn0.3O3	16.5	52(800℃)
Gd0.7Ca0.3MnO3	very low, nonlinear	27(800℃)
Gd0.7Sr0.3MnO3	9.5	83(800℃)
Gd0.8Sr0.2Co0.2Mn0.8O3	10.5	28(800℃)
Gd0.8Sr0.2Co0.9Mn0.1O3	24	271(800℃)
Gd0.8Sr0.2MnO3	very low, nonlinear	28
La0.6Sr0.4MnO3	12.7	320(800℃)
La0.76Sr0.19Mn0.7Ni0.3O3	14.05
La0.7Sr0.3MnO3	11.7	178(800℃);240(800℃)[2]	2×10-13（897℃）		[2]C.Sun,R B.Justin Roller.J Solid State Electrochem (2010) 14:1125
La0.82Sr0.16Mn0.7Ni0.3O3	11.7	68(900℃)
La0.84Sr0.16Mn0.6Co0.4O3	13.65	45(800℃)
La0.84Sr0.16Mn0.6Fe0.4O3	11.55	18(800℃)
La0.84Sr0.16Mn0.8Co0.2O3	11.69	47(800℃)

首页上一页下一页末页第1页/ 共3页

转至页

生产工艺

材料牌号	原材料	制备方法	信息来源
Grade	Raw materials	Preparation Processes	Information Source
Gd0.5Sr0.5MnO3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
Gd0.7Ca0.3Co0.4Mn0.6O3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
Gd0.7Ca0.3Co0.7Mn0.3O3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
Gd0.7Ca0.3MnO3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
Gd0.7Sr0.3MnO3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
Gd0.8Sr0.2Co0.2Mn0.8O3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
Gd0.8Sr0.2Co0.9Mn0.1O3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
Gd0.8Sr0.2MnO3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
La0.6Sr0.4MnO3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
La0.76Sr0.19Mn0.7Ni0.3O3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
La0.7Sr0.3MnO3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
La0.82Sr0.16Mn0.7Ni0.3O3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
La0.84Sr0.16Mn0.6Co0.4O3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
La0.84Sr0.16Mn0.6Fe0.4O3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法
La0.84Sr0.16Mn0.8Co0.2O3	相应金属氧化物或者碳酸盐；相应金属硝酸盐，柠檬酸或者甘氨酸，EDTA	固相法;柠檬酸-硝酸盐法或者溶胶-凝胶法